数控采暖锅炉延长寿命使用方法
    2013-10-14 9:03:06  文章来源:http://www.jnlzsb.com
     

    数控采暖锅炉停用后放掉水,清除污物,烘干金属表面。然后在金属表面均匀地涂上一层防腐涂料,以防止锅炉的停用腐蚀。防腐涂料一般采用黑铅粉(其主要成份为碳黑与滑石粉)与机油(40*50*均可)按一定比例配成。一般可按黑铅粉:机油:12的配比调合而成。 涂复时,要求凡能接触到的部位,都要均匀地涂附。

    Water to remove dirt, let NC heating boiler after drying, the metal surface. Then on the metal surface is uniformly coated with a layer of anticorrosive coating, to prevent corrosion of boiler. Anticorrosive paint for general use black powder (the main component is carbon black and talcum powder) and oil (40* or 50* may) in a certain proportion. According to the general black powder: Oil: 1 2 blending into. Coating, ask who can contact to the site, are evenly coated.

    数控采暖锅炉管内不易接触的部位,可利用钢丝缠上棉纱,醮取涂料上下牵拉的方法涂附。采用涂料防腐法,若对蒸汽品质有一定的要求时,应在锅炉(工业清洗|化学清洗|锅炉清洗|换热器清洗)启动前采用碱煮法(每吨水加磷酸三钠或纯碱58kg)煮沸810小时。并加强表面排污,将涂料去除。此法经济、简单、效果好,适用于长期停炉保养。

    NC heating boiler tube is not easy to contact the site, can use steel wire cotton yarn, pulling out coating method of coating. The use of paint protection, if certain requirements on the quality of steam, should be in the boiler (industrial cleaning | | boiler chemical cleaning cleaning | heat exchanger cleaning) before the start of the alkali cooking method (per ton of water with three sodium phosphate or sodium carbonate is 5 ~ 8kg) boil for 8 to 10 hours. And to strengthen the surface discharge, the coating removal. This method is economical, simple, good effect, suitable for long-term shutdown maintenance.

    数控采暖锅炉清洗剂的使用方法:

    1、将除垢剂与水按110的比例稀释注入锅炉进水口;

    2、将水注满至最高水位,等待4小时,使除垢剂溶液充分和水垢反应;

    3、打开排污出口,排干清洗液(工业清洗|化学清洗|锅炉清洗|换热器清洗);

    4、注入清水冲洗至水清,清洗除垢工作完成。   

    提示:   

    10.5吨锅炉推荐除垢剂用量10公斤 

    2、锅炉超过2年未清洗,请延长清洗时间或者加大用量

    350度左右热水清洗,效果更佳

    相关阅读:数控采暖锅炉使用详细说明